{"id":11575,"date":"2021-04-02T06:05:30","date_gmt":"2021-04-02T12:05:30","guid":{"rendered":"https:\/\/www.ulprospector.com\/knowledge\/?p=11575"},"modified":"2021-04-30T07:54:51","modified_gmt":"2021-04-30T13:54:51","slug":"pc-radiation-cure-coatings-the-ultimate-in-rapid-cure-technology","status":"publish","type":"post","link":"https:\/\/ulprospector.ul.com\/11575\/pc-radiation-cure-coatings-the-ultimate-in-rapid-cure-technology\/","title":{"rendered":"Radiation Cure Coatings \u2013 The Ultimate in Rapid Cure Technology"},"content":{"rendered":"

\"TheRadiation cure coatings offer a high-speed light curing process with a number of advantages over more conventional cure processes. Multiple advantages include\u00a0<\/em><\/strong>high speed, lower energy requirements, little- or no-VOC, less production space, less dirt collection, high quality finish, rapid processing\u00a0as well as instant on-off with some UV light technologies also expedite production and energy savings. Electron and UV\u00a0curable\u00a0<\/a>paint finishes have existed since the 1960s and are based on polymerization reactions including free radical and cation-initiated chain-growth polymerization. As the majority of coatings for UV cure coating utilize free radical polymerization (>90% of market), this article will focus primarily on free radical polymerization initiated by a photoinitiator <\/a>(Fig. 1):<\/p>\n

\"UV<\/p>\n

\u00adThe types of unsaturation used in UV\/EB cure coatings are provided in Table I, with by far the largest type being acrylate<\/a>.<\/p>\n

\"\"
Table I \u2013 Type of Unsaturation used in UV\/EB Cure<\/figcaption><\/figure>\n

Photoinitiator<\/em><\/strong>\u00a0considerations primarily include two different characteristics of the photoinitiator\u2019s absorption curve. First, is the maximum wavelength (Lambda Max) of light that is absorbed by the PI and second, the strength of this absorption (molar extinction coefficient).\u00a0Photoinitiators\u00a0<\/a>developed for curing pigmented films normally have higher molar extinction coefficients at longer wavelengths between 300 nm to 450 nm than those for curing clear formulations. To maximize cure and efficiency, the PI\u2019s absorbance must match the light output of the lamp as different lamps have different spectral outputs (see Table I). Longer wavelength light is also essential to enhance cure in thicker coatings. Newer PI\u2019s have also enabled the formulation of pigmented coatings in addition to that of clear coatings. The general cure considerations influenced by color, PVC, pigment particle size and film thickness are summarized in Fig. 2:<\/p>\n

\"factors
Figure 2 \u2013 UV Cure Considerations. Image: Ciba \u2013 Geigy literature<\/figcaption><\/figure>\n

There are two main types of free radical\u00a0<\/em><\/strong>photoinitiators, Type I and Type II. Type I photoinitiators<\/a> undergo cleavage upon irradiation to form two free radicals. Normally only one of these free radicals is reactive and thus initiates polymerization. 1-hydroxy-cyclohexylphenyl-ketone is a widely used Type I PI. Type II photoinitiators<\/a> form an excited state upon irradiation and abstract an atom or electron from a donor molecule (synergist). The donor molecule in turn initiates polymerization. An example of a widely used Type II photoinitiator is benzophenone<\/a>. Tertiary amines<\/a> are typically used as synergists as they react with benzophenone, and also retard the inhibition of polymerization by oxygen. Acrylated tertiary amine<\/a> compounds are used when odor and extractables are of concern. Oxygen can also inhibit cure especially in thin films; to counteract oxygen inhibition, coatings can use amine synergists, be cured under a nitrogen atmosphere, employ the addition of wax, high initiator concentration, more intense UV Light, and\/or surface-active initiators.<\/p>\n

Other key ingredients that determine the performance of UV Cure formulations include UV curable monomers and oligomers. Figure 3 illustrates typical monomers<\/a> that are used along with performance characteristics.<\/p>\n

\"monomers<\/p>\n

Table II. General Performance Versus Monomer<\/p>\n

\"general
Figure 3. Typical Monomers and Performance Characteristics<\/figcaption><\/figure>\n

There are a number of UV curable oligomer<\/a> types available as well depending on the type of performance desired, please refer to Fig. 4 for a listing of some of the common oligomer types available along with an overview of performance characteristics.<\/p>\n

Electron Beam cure coatings can be used to cure acrylate functional coatings. As the energy used is much higher (150 \u2013 300 keV) than that in UV cure, a photoinitiator is not necessary. Other advantages of EB cure over UV is that pigments do not adversely effect the cure. The vehicle systems that are used are essentially the same as that used in UV curing (acrylates) and vehicles used for UV cationic cure. Disadvantages of EB curing include the high cost of capital equipment and curing must be done in an inert environment. The coating resin once irradiated forms a radical cation and a secondary electron the excited state CR* can then homolytically cleave to form a free radical and initiate polymerization.<\/p>\n

\"Radiation<\/p>\n

\"oligomer
Figure 4 \u2013 UV Cure Oligomer Types\/Characteristics<\/figcaption><\/figure>\n

In addition to 100% solid liquid UV coatings, other UV types include waterborne UV and powder UV. Waterborne UV curables<\/a> have advantages over conventional UV cure as no reactive diluent is necessary to control viscosity. Also, as opposed to conventional UV cure formulations, the viscosity of the coating is independent of the molecular weight of the resin<\/a> and for spray application viscosity, solids are adjusted by adding water rather than low viscosity reactive monomer. In addition, since there are fewer double bonds to cure, shrinkage is lower and can thus improve adhesion. The main disadvantage is that the water needs to be removed by passing through an oven at about 80\u00b0C prior to UV curing. In powder UV cure coatings, the part is sprayed electrostatically. Automatic guns are recommended over manual application to ensure an even, consistent film thickness is applied. Next, the applied coating is baked in a convection, IR or oven to melt and flow the powder. This step is at a much lower temperature and less time (175-280 \u00b0F for a few seconds instead of 320-390\u00b0F for 5 to 20 minutes) for conventional powder coating. Once the powder is melt flowed, the parts enter a UV cure chamber that cure the coating in seconds instead of minutes, as with traditional thermal powder.<\/p>\n

Cationic UV cure coatings have the following advantages:<\/p>\n